316L316 Cold Rolled Stainless Steel sheets(0.2mm-8mm)
Huaxiao Capacity about 316L 316 cold rolled stainless steel sheets, 316 316L CRC
Thickness: 0.2mm - 8.0mm
Width: 300mm - 6000mm, the narrowed products pls check in strip products
Package weight: 1.0-3.0MT
Finish: 2B,2D
316 Same grade from different country standard
06Cr17Ni12Mo2 0Cr17Ni12Mo2 S31600 SUS316 1.4401
316 Chemical component ASTM A240 :
C?≤0.08 ?Si ?≤0.75 ?Mn ?≤2.0 ? S ?≤0.03 ?P ?≤0.045, Cr ?16.0?18.0 ?Ni ?10.0?14.0?
Mo: 2.0-3.0, N≤0.1
316 mechanical property ASTM A240 :
Tensile strength : > 515 Mpa
Yield Strength : >205 Mpa
Elongation (%): > 40%
Hardness: < HRB95
316L Same grade from different country standard
1.4404 022Cr17Ni12Mo2 00Cr17Ni14Mo2 S31603 SUS316L
316L Chemical Component ASTM A240 :
C?≤0.03 ?Si ?≤0.75 ?Mn ?≤2.0 ? S ?≤0.03 ?P ?≤0.045, Cr ?16.0?18.0 ?Ni ?10.0?14.0?
Mo: 2.0-3.0, N≤0.1
316L Mechanical Property ASTM A240 :
Tensile strength : > 485 Mpa
Yield Strength : >170 Mpa
Elongation (%): > 40%
Hardness: < HRB95
General Description about 316/316L Stainless Steel sheets
316L is a kind of molybdenum-containing stainless steel. Due to the molybdenum content in steel, the total performance of this steel is better than that of 310 and 304 stainless steel. Under high temperature conditions, when the concentration of sulfuric acid is lower than 15% or higher than 85%, 316L stainless steel has a wide range. use. 316L stainless steel also has good resistance to chloride attack and is therefore commonly used in marine environments.
316L stainless steel has a maximum carbon content of 0.03 and can be used in applications where annealing is not possible and maximum corrosion resistance is required.
Corrosion resistance
Corrosion resistance is better than 304 stainless steel, with good corrosion resistance in the production process of pulp and paper. Moreover, 316L stainless steel is also resistant to erosion by marine and aggressive industrial atmospheres.
Heat resistance
316L stainless steel has good oxidation resistance in intermittent use below 1600 °C and continuous use below 700 °C. In the range of 800-1575 degrees, it is best not to continue to act. 316L stainless steel, but when 316L stainless steel is continuously used outside this temperature range, the stainless steel has good heat resistance. 316L stainless steel has better carbide precipitation resistance than 316 stainless steel and can be used in the above temperature range.
Heat treatment
The solution annealing is performed in a temperature range of 1010-1150 degrees, and then rapidly cooled. 316L stainless steel cannot be hardened by heat treatment.
Welding performance
316L stainless steel has good welding properties. All standard welding methods can be used for welding. When welding, 316Cb, 316L or 309Cb stainless steel filler rods or welding rods can be used for welding according to the application. For best corrosion resistance, the welded section of 316 stainless steel requires post-weld annealing. If 316L stainless steel is used, post-weld annealing is not required.